ST37 ST35 ST52 yuqori aniqlikdagi po'lat quvur trubkasi
Din 2391 Choksiz po'lat quvur (Din 2391, En 10305-1, en 10305-4, BS 6323 nozik choksiz po'lat quvur NBK GBK)
Spetsifikatsiya
| Standart | DIN2391 DIN1630 DIN2448 |
| Baho | ST35/E235 ST37.4 ST45/E255 ST52/E355 |
| Yetkazib berish sharti | NBK(+N) BK(+C) GBK(+A) BKW(+LC) BKS(+SR) |
| Hajmi | OD: 4 dan 219 mm gacha Qalinligi 0,5-35 mm, Uzunligi: 3 m, 5,8,6 yoki talablarga muvofiq |
| Tugatish | Galvanizli sirt (silver/sariq/rangli) 8-12um sink qoplamasi |
| Ilova | Gidravlik tizim;Avtomobil / avtobus;qurilish vositasi |
| Yetkazib berish vaqti | A.3 kun, agar bu tovar birja tovarlari bo'lsa. B. Miqdoriga ko'ra taxminan 30 kun |
Yuzaki ishlov berish
1. Yalang'och trubka (qoplamasiz): Yorqin va silliq
A. Kumush ruxlangan
B. Sariq galvanizli
C. Zaytun yashil qoplangan
Qatlam qalinligi: 8-20um, tuzli buzadigan amallar sinovi: 48-150 soat
3. Qora fosfat
Turli maydonlar
1. Avtomobil sohalari
A. Yoqilg'i quyish liniyalari/nozullari
B. CNG (siqilgan tabiiy gaz) trubkasi - portlash bosimi: 1307 bar, ish bosimi: 350 bar atrofida
C. Drayv uzatish: Rulda ustuni elementlari
D. Tishli vallar, qo'l tormozi, old akslar, havo yostig'i ingalyatorlari, stabilizatorlar, o'rindiqlarni mahkamlagichlar, old g'ildirak vallar
2. Gidravlik maydonlar
A. Shlangi sxemalar (HPL), pnevmatik liniyalar va gidravlik suspenziya
B. Gidravlik silindrlar (HPZ)
Kimyoviy tarkibi
| Chelik darajasi | C | Si | Mn | P | S | Al | |
| Ism | Yo'q. | maks | maks | maks | maks | maks | maks |
| ST35 | 1.0308 | 0,17 | 0,35 | 0,4（min） | 0,025 | 0,025 | — |
| ST45 | 1.0408 | 0,21 | 0,35 | 0,4（min） | 0,025 | 0,025 | — |
| ST52 | 1.058 | 0,22 | 0,55 | 1.6 | 0,025 | 0,025 | — |
Mexanik xususiyatlar
| Chelik darajasi | Hosildorlik kuchi (Mpa) | Kuchlanish kuchi (Mpa) | Uzayish（%） | |
| Ism | Yo'q. | ReH (daq) | Rm(daq) | A(min) |
| ST35 | 1.0308 | 235 | 340 dan 480 gacha | 25 |
| ST45 | 1.0408 | 255 | 440 dan 570 gacha | 21 |
| ST52 | 1.058 | 355 | 490 dan 630 gacha | 22 |
Tolerantlik
| OD | Ruxsat etilgan bardoshlik | Maxsus bag'rikenglik | ||
|
| GB/T3639 | DIN2391 | OD | WT |
| 4 mm-20 mm | ±0,10 mm | ±0,08 mm | ±0,05 mm | ±0,05 mm |
| 20 mm-30 mm | ±0,10 mm | ±0,08 mm | ±0,08 mm | ±0,08 mm |
| 31-40 mm | ±0,15 mm | ±0,15 mm | ±0,10 mm | ±0,08 mm |
| 41-60 mm | ±0,20 mm | ±0,20 mm | ±0,15 mm | ±0,15 mm |
| 61-80 mm | ±0,30 mm | ±0,30 mm | ±0,20 mm | ±0,20 mm |
| 81-120 mm | ±0,45 mm | ±0,45 mm | ±0,30 mm | ±0,30 mm |
Yetkazib berish sharti
| Belgilanish | Belgi | Tavsif |
| Sovuq tugagan (qattiq) | BK(+C) | Quvurlar oxirgi sovuq shakllanishdan keyin issiqlik bilan ishlov berilmaydi va shuning uchun deformatsiyaga nisbatan ancha yuqori qarshilikka ega |
| Sovuq tugagan (yumshoq) | BKW | Yakuniy issiqlik bilan ishlov berishdan so'ng cheklangan deformatsiyani o'z ichiga olgan sovuq chizish amalga oshiriladi.Tegishli keyingi ishlov berish ma'lum darajada sovuq shakllanish imkonini beradi (masalan, egilish, kengayish) |
| (+LC) | ||
| Sovuq tugagan va stressdan xalos bo'lgan | BKS(+SR) | Issiqlik bilan ishlov berish oxirgi sovuq shakllanish jarayonidan keyin qo'llaniladi.Tegishli ishlov berish shartlariga rioya qilgan holda, qoldiq kuchlanishlarning ortishi ma'lum darajada shakllantirish va ishlov berish imkonini beradi. |
| Tavlangan | GBK(+A) | Oxirgi Sovuq shakllantirish jarayoni nazorat ostida atmosferada tavlanishdan so'ng amalga oshiriladi. |
| Normallashtirilgan | NBK(+N) | Oxirgi sovuq shakllanish jarayoni boshqariladigan atmosferada yuqori transformatsiya nuqtasi ustidagi tavlanishdan so'ng amalga oshiriladi. |
Sifatni tekshirish
1. DIN2391/EN10305 yoki boshqa standartlarga muvofiq qat'iy.
2. Namuna: Namuna sinov uchun bepul.
3. Sinovlar: Tuz purkash testi / Uzilish testi / Eddy oqimi / Kimyoviy tarkib testi mijozlar talabiga binoan
4.Sertifikat: IATF16949, ISO9001, SGS va boshqalar.
5.EN 10204 3.1 Sertifikatlash
Mahsulotni qadoqlash